Binder

Name Chemical characterization Appearance Dry solids Viscosity pH Density Net charge Tg-Value E-Modulus
Epamin VAE 60 Ethylene/vinylacetatecopolymerdispersion white dispersion 60 ± 1 3800 ± 1000 4.5 ± 1 1,07 ± 0.03 n ca. 3°C -
EVA dispersion for the formulation of ink jet receiving layers and the coating and finishing of textiles. Excellent flow properties, fast set off. Can be combined with any other disperion.
Acetolan LP 909 Modified polyvinylacetatedispersion white dispersion 55 ± 2 3000 ± 1500 4.5 ± 1 1,09 ± 0.03 n ca. 33°C -
Acrylan LS 283 Silanated Polyvinylalcohol clear liquid 30 ± 1 2500 ± 1000 5.0 ± 1 1,04 ± 0.03 n - -
Silanated PVOH for the formaultion of cationic ink jet receiving layers. Low molecular weight.
Acrylan LS 285 Silanated Polyvinylalcohol clear liquid 25 ± 1 2500 ± 1000 5.0 ± 1 1,04 ± 0.03 n - -
Silanated PVOH for the formaultion of cationic ink jet receiving layers. Mid molecular weight.
Acrylan LS 287 Silanated Polyvinylalcohol clear liquid 13 ± 1 3000 ± 1500 5.0 ± 1 1,04 ± 0.03 n - -
Silanated PVOH for the formaultion of cationic ink jet receiving layers. High molecular weight.
PU-Coat DMP 10 Aliphatic Polyester-PU-Dispersion white dispersion 50 ± 2 50 - 800 7.5 ± 1 1,10 ± 0.03 a -42°C 2,1 MPa
PUD for the formulation of textile coatings. High film flexibility, suitable for mechanical foaming, good alcohol resistance and good lightfastness.
PU Coat DMP 30 Aliphatic Polyester-PU-Dispersion white dispersion 40 ± 1 50 - 600 7.0 ± 1 1,10 ± 0.03 a -54°C 2 MPa
PUD for the formulation of textile coatings. High film flexibility,suitable for mechanical foaming, good alcohol resistance and good lightfastness.
PU Coat DMP 40 Aliphatic Polyester-PU-Dispersion white dispersion 59 ± 2 50 - 600 7.0 ± 1 1,10 ± 0.03 a -4°C 1,3 MPa
PUD for the formulation of textile coatings. Outstanding resistance to hydrolysis, good adhesion, high solids content, very good stirring stability, suitable for mechnaical foaming, high light fastness, soft handle.
PU-Coat DMP 50 Aliphatic Polycarbonateesterpolyether-PUD white dispersion 60 ± 2 150 - 800 8.0 ± 1 1,10 ± 0.03 a -69°C 2-3 MPa
PUD for the formulation of textile coatings. High solids content, outstanding resistance to hydrolysis, crosslinkable, suitable for mechanical foaming, high scratch resistance, good light fastness, high resistance to cracking.
PU-Coat DMP 65 Aliphatic Polyether-PU-Dispersion white dispersion 40 ± 1 50 - 600 6.5 ± 1 1,10 ± 0.03 a -37°C 5 MPa
PUD for the formulation of textile coatings. High film flexibility, good alcohol resistance, good lightfastness, very good forces.
PU-Coat DMP 75 Aliphatic Polyether-PU-Dispersion white dispersion 59 ± 2 50 - 600 7.5 ± 1 1,10 ± 0.03 a -42°C 2,5 MPa
PUD for the formulation of textile coatings. High film flexibility, suitable for mechanical foaming, good alcohol resistance and good lightfastness.
PU-Coat DMP 80 Aliphatic Polycarbonatester-PU-Dispersion white dispersion 40 ± 1 150 - 800 7.5 ± 1 1,10 ± 0.03 n -33,5°C 5 MPa
PUD for the formulation of textile coatings. Good resistance to hydrolysis, high scratch resistance, high ageing resistance, good light fastness, high resistance to cracking.
PU-Coat DMP 105 Aliphatic Polyester-PU-Dispersion white dispersion 40 ± 1 50 - 600 7.5 ± 1.5 1,10 ± 0.03 a -33°C 13 MPa
PUD for the formulation of textile coatings. Good resistance to hydrolysis, high scratch resistance, dry surface.
PU-Coat DMP 110 Aliphatic Polyether-PU-Dispersion white dispersion 40 ± 1 150 - 800 7.5 ± 1.5 1,10 ± 0.03 a -49,5°C 9 MPa
PUD for the formulation of textile coatings. High scratch resistance, good light fastness, dry surface.
PU-Coat DMP 115 Aromatic Polyether-PU-Dispersion white dispersion 35 ± 1 50 - 1000 8.0 ± 1 1,10 ± 0.03 a -50°C 2 MPa
PUD for the formulation of textile coatings. Good adhesion, Tie-Coat for PU-Coat high-solids systems.
PU Coat 42 Aliphatic Polyester-PU-Dispersion white dispersion 50 ± 2 150 - 800 7.0 ± 1 1,07 ± 0.03 a -4°C 1,3 MPa
PUD for the formulation of textile coatings. Good resistance to hydrolysis, good adhesion, suitable for mechanical foaming, good light fastness, soft handle.
PU Coat 53 Polyurethanedispersion white dispersion 40 ± 1 50 - 600 7.5 ± 1 1,07 ± 0.03 a -50°C 6,9 MPa
PUD for the wet bonding of textile substrates. Very suitable for applications involving flexibilised PVC substrates. Soft film and low activation temperature.
PU-Coat 96 High molecular weight PU-Dispersion white dispersion 50 ± 2 50 - 900 7.5 ± 1.5 1,10 ± 0.03 a -50°C 5,6 MPa
PUD for the formulation of heat activatable adhesive.