Crosslinker/Curing Agents

Name Chemical characterization Appearance Dry solids Viscosity pH Density Net charge Particle size
Eporit L 100 Bisphenol-A-diglycidetheremulsion white dispersion 60 ± 1 4500 ± 500 6.5 ± 1 1,05±0.03 n 1-5µm
BPA Epoxy resin emulsion with high electrolyte stability for high-wet strengt and alkali resistant paper coatings. Excellent crosslinker for carboxylated SB- and SA-dispersions. Also used for bonding improvement in texile finishing and coating.
Eporit L 100/80 Bisphenol-A-diglycidetheremulsion white dispersion 80 ± 1 5500 ± 500 6.5 ± 1 1,13±0.03 n 1-5µm
High solids epoxy resin emulsion for application in paper, textile and construction industry
Eporit L 120 Novalacbased epoxyresin emulsion white dispersion 55 ± 1 3000 ± 1000 6.5 ± 1 1,05±0.03 n 1-5µm
Novolacbased epoxy resin emulsion with high UV stability for corrosion protection.
Eporit AF 100 Bisphenol-A/F-diglycidetheremulsion white dispersion 60 ± 1 4500 ± 500 6.5 ± 1 1,05±0.03 n 1-5µm
BPA/F Epoxy resin emulsion with high electrolyte stability for high-wet strengt and alkali resistant paper coatings. Excellent crosslinker for carboxylated SB- and SA-dispersions. Also used for bonding improvement in texile finishing and coating.
Eporit F 100 Bisphenol-F-diglycidetheremulsion white dispersion 60 ± 1 4500 ± 500 7.0 ± 1 1,05±0.03 n 1-5µm
BPF Epoxy resin emulsion with high electrolyte stability for high-wet strengt and alkali resistant paper coatings. Excellent crosslinker for carboxylated SB- and SA-dispersions. Also used for bonding improvement in texile finishing and coating.
Eporit GE 45 Pentaerythrite-Epichlorohydrinepolymer yellowish liquid ca. 99 1050 ± 150 - 1,24 ± 0.02 n -
Epoxy resin for high-wet strengt and alkali resistant paper coatings. Excellent crosslinker for carboxylated SB- and SA-dispersions. Improves water and alkali resistance of coated papers. Also used for bonding improvement in texile finishing and coating.
Eporit DMP 30 2,4,6-Tri-(dimethylaminoethyl)phenol yellowish liquid 100 150 ± 75 - 0.98 ± 0.03 - -
Hardener used for Epoxy resins emulsions. Interacts preferentially with carboxyl- and hydroxilgroups.
Eporit EH 45 Polyamideamineemulsion white dispersion 55±2 200 ± 100 7.0 ± 1 1.08 ± 0.03 - -
Waterborne Polyamideamineemulsion for 2K-systems. Pot life 6-8 hours. Quick drying.
TexCross AI 45 Blocked Aliphatic Polyisocyanate - 40 ± 1 < 1500 7.5 ± 1 - - -
Reactive blockes crosslinker with improved reactivity, co-solvent free and thermostability (yellowing) for PU-based textile coatings. Deblocking temperature 120°C.
TexCross HM 45 Hydrophilic aliphatic Polyisocyanate - 100 1250 ± 300 - 1.15 ± 0.03 - -
HDI-based Polyisocyanate emulsifiable in almost all kinds of polymer dispersions. Increases the chemical and mechanical resistance of the bonds.
TexCross IB 25 Waterborne Suspension of a TDI-Dimer - 40 ± 1 < 1000 9.5 ± 1 1.15 ± 0.03 - -
Crosslinker for the production of latently-reactive adhesive films.
TexCross IP 100 Aliphatic Polyisocyanate - 100 730 ± 300 - 1.15 ± 0.03 - -
HDI-based Polyisocyanate showing very good chemical and mechanical resistance. Interacts best with Polyacrylate- or Polyesterpolyols.
TexCross IP 105 Hydrophilic aliphatic Polyisocyanate - 100 2800 ± 800 - 1.16 ± 0.03 - -
HDI-based Polyisocyanate used as crosslinker for polyol-based binder. Self emulsifying in water due to ist hydrophilic character.